Bleed resistant cyanate ester-containing compositions

ABSTRACT

In accordance with the present invention, there are provided adhesive formulations containing small amounts of bleed control agent, which render the invention compositions extremely resistant to resin bleed. Several different types of bleed control agents are contemplated for use in the practice of the present invention, e.g., cationic surfactants, tertiary amines, tertiary phosphines, amphoteric surfactants, polyfunctional compounds, and the like, as well as mixtures of any two or more thereof.

RELATED APPLICATIONS

This application is a continuation-in-part of U.S. Ser. No. 08/439,975, filed May 12, 1995, now abandoned, the entire contents of which are hereby incorporated by reference herein.

FIELD OF THE INVENTION

The present invention relates to adhesive compositions. In a particular aspect, the present invention relates to modified adhesive compositions having reduced propensity to bleed upon application to a substrate.

BACKGROUND OF THE INVENTION

Monomer vehicles used in die attach paste compositions tend to bleed out onto the substrate during cure, and even (in some cases) during room temperature staging of the adhesive. Indeed, resin bleed is a serious issue for die attach in electronic packaging. "Bleed" is defined herein as separation of the monomer vehicle phase and filler during staging or cure, resulting in spread of resin away from the die bond area. Resin bleed can generate wire bond non-sticks if it flows up onto bonding pads of the microelectronic device itself or the package into which it has been placed.

There are several potential impacts of this problem, e.g., a package assembler must deal with the likelihood of reduced product yields (and the attendant increased costs for manufacture), the part-to-part variability of the bleed phenomenom results in unacceptable part-to-part variability of the desired product, thereby necessitating the additional expense of 100% visual inspection of each component before being passed onto the wire bond step, and the like.

U.S. Pat. No. 4,483,898, issued to Harold Schonborn, et.al., and assigned to AT&T, discloses the use of alcohols, amides, amines, carboxylic acids, and esters containing two to twelve carbon atoms as allegedly being effective for the reduction of spreading of liquid films on substrates. The inhibition of resin bleed for epoxy, acrylate and silicone adhesive systems was the specific focus of this patent. The preferred bleed inhibiting compounds were poly-fluorinated (i.e. where most or all of the hydrogens of the hydrocarbon residue had been replaced by fluorine). The effective range contemplated by this patent is 0.05 to 5% by weight of the liquid phase. It is interesting to note, however, that the bleed control failed at 0.2% by weight of the most preferred bleed inhibiting agent in the absence of any "coupling agent" (see example VII). Furthermore, several of the compounds cited in '898 had deleterious effects on the pot life of the epoxy systems in which they were used (see, for example, Example VIII).

Accordingly, there is still a need in the art for compositions and methods useful for reducing the occurrence of resin bleed when die-attach compositions are applied to a substrate.

BRIEF DESCRIPTION OF THE INVENTION

In accordance with the present invention, we have discovered that the addition of small amounts of bleed control agent(s) to adhesive formulations renders such compositions extremely resistant to resin bleed. Several different types of bleed control agents are contemplated for use in the practice of the present invention, e.g., cationic surfactants, tertiary amines, tertiary phosphines, amphoteric surfactants, polyfunctional compounds, and the like, as well as mixtures of any two or more thereof.

DETAILED DESCRIPTION OF THE INVENTION

In accordance with the present invention, there are provided compositions for attaching a device to a substrate. Invention compositions comprise:

a monomer vehicle comprising at least one polycyanate ester monomer;

a quantity of a bleed control agent sufficient to reduce resin bleed upon application of said composition to a substrate; and optionally

a metal catalyst.

Invention compositions can optionally contain filler material. Fillers contemplated for use in the practice of the present invention can be thermally and/or electrically conductive, and can be present in widely varying amounts, typically falling in the range of about 20 to about 92 wt. percent, based on the total weight of the attach paste.

Examples of electrically conductive fillers contemplated for use in the practice of the present invention include, for example, silver, nickel, cobalt, copper and aluminum fillers, as well as alloys of such metals. Both powder and flake forms of filler may be used in the attach paste compositions of the present invention. The preferred thickness of flake is under 2 microns with a dimension of about 20 to about 25 microns. Flake employed herein preferably has a surface area of about 0.15 to 5.0 m² /g and a tap density of 0.4 to 5.5 g/cc. Powder employed herein preferably has a diameter of about 0.5 to 15 microns.

Cyanate ester monomers contemplated for use in the practice of the present invention contain two or more ring forming cyanate (--O--C.tbd.N) groups which cyclotrimerize to form substituted triazine rings upon heating. Because no leaving groups or volatile byproducts are formed during curing of the cyanate ester monomer, the curing reaction is referred to as addition polymerization. Suitable polycyanate ester monomers that may be used in the practice of the present invention include, for example, 1,1-bis(4-cyanatophenyl)methane, 1,1-bis(4-cyanatophenyl)ethane, 2,2-bis(4-cyanatophenyl)propane, bis(4-cyanatophenyl)-2,2-butane, 1,3-bis[2-(4-cyanato phenyl)propyl]benzene, bis(4-cyanatophenyl)ether, 4,4'-dicyanatodiphenyl, bis(4-cyanato-3,5-dimethylphenyl)methane, tris(4-cyanatophenyl)ethane, cyanated novolak, 1,3-bis[4-cyanatophenyl-1-(1-methylethylidene)]benzene, cyanated phenoldicyclopentadiene adduct, and the like. Polycyanate ester monomers utilized in accordance with the present invention may be readily prepared by reacting appropriate dihydric or polyhydric phenols with a cyanogen halide in the presence of an acid acceptor.

Monomers that can optionally be combined with polycyanate ester monomer(s) in accordance with the present invention are selected from those monomers which undergo addition polymerization. Such monomers include vinyl ethers, divinyl ethers, diallyl ethers, dimethacrylates, dipropargyl ethers, mixed propargyl allyl ethers, monomaleimides, bismaleimides, and the like. Examples of such monomers include cyclohexanedimethanol monovinyl ether, trisallylcyanurate, 1,1-bis(4-allyloxyphenyl)ethane, 1,1-bis(4-propargyloxyphenyl)ethane, 1,1-bis(4-allyloxyphenyl-4'-propargyloxyphenyl)ethane, 3-(2,2-dimethyltrimethylene acetal)-1-maleimidobenzene, 2,2,4-trimethylhexamethylene-1,6-bismaleimide, 2,2-bis[4-(4-maleimidophenoxy)phenyl]propane, and the like.

Various monomers may be combined to obtain a liquid monomer vehicle, without the need for any added solvent/diluent, such as alkylphenol. For example, when 1,1-bis(4-cyanatophenyl)ethane, having a melting point of 29° C., and 2,2,4-trimethylhexamethylene-1,6-bismaleimide, having a melting point range of 75° to 125° C., were combined (in the absence of alkylphenol), mixtures containing up to 12 wt. percent bismaleimide were found to remain liquid indefinitely. The lowest melting mixture contained 8 wt. percent bismaleimide and had a melting point of 26.07° C., which is three degrees below the melting point of 1,1-bis(4-cyanatophenyl)ethane. The viscosity of this mixture was lower than that of the pure dicyanate ester. Surprisingly, the thermal stability of polymer derived from this mixture exceeded the thermal stability of the polycyanate ester homopolymer. Thermal stability was determined using thermogravimetric analysis run at a temperature ramp rate of 10° C./minute under an air purge. The decomposition onset temperature for the polymer derived from the mixture was 438° C., whereas the decomposition onset temperature for the homopolymer was 419° C.

Metal catalysts employed in the practice of the present invention are metal acetylacetonates which are metal chelates wherein the preferred metal is a transition metal. Examples of suitable metals employed herein are cobalt, manganese, tin, zinc, copper and nickel, all in the divalent state; manganese, iron, cobalt and aluminum, all in the trivalent state; and tetravalent titanium. The presently most preferred metal catalyst is cobalt(III) acetylacetonate. Typically, the metal catalyst is present in the range of about 50 to about 1500 ppm.

As employed herein, the term "bleed control agent" refers to a variety of additives which, acting alone or in combination, reduce and/or inhibit the propensity of monomer vehicle phase and filler to separate. Examples of the types of compounds contemplated for use in the practice of the present invention as bleed control agents include cationic surfactants, tertiary amines, tertiary phosphines, amphoteric surfactants, polyfunctional compounds, and the like, as well as mixtures of any two or more thereof.

Those of skill in the art recognize that the quantity of bleed control agent employed in the practice of the present invention can vary widely, typically falling in the range of about 0.1 up to about 10 wt % of the organic fraction of the cyanate ester-containing composition (i.e., the unfilled organic vehicle).

Additives contemplated for use in the practice of the present invention include higher molecular weight, tetravalent nitrogen compounds (where the nitrogen atom bears a positive charge). Examples of such compounds include quaternary ammonium salts where the hydrocarbon residues attached to the nitrogen comprise linear alkyl, branched alkyl, linear alkenyl, branched alkenyl, benzyl, cycloaliphatic, ethyl hydroxy, propyl hydroxy, polyalkylene oxide and phenyl substituted alkyl groups. The nitrogen, furthermore, may be incorporated into a cyclic structure such as a pyridine, a piperazine, a piperidine, a pyrazine, a pyrimidine, a quinoline, an isoquinoline, an imidazole, and the like, or any substituted analogs thereof. The counter ion for the quaternized ammonium cation may be any anion other than fluoride or chloride. The counter ion may also be covalently linked to the nitrogen by a carbon containing bridging group as in the case of betaines, sulfobetaines, N-alkylaminopropionic acids, N-alkyliminodipropionic acids, imidazoline carboxylates, tertiary amine oxides and tertiary phosphine oxides (i.e. amphoteric, or zwitterionic surfactants).

Cationic surfactants contemplated for use in the practice of the present invention include quaternary onium compounds (e.g., quaternary ammonium compounds, quaternary phosphonium compounds, or mixtures of any two or more thereof). Preferably, quaternary onium compounds employed in the practice of the present invention have in the range of about 15 up to about 100 total carbon atoms, with quaternary onium compounds wherein at least one side chain thereof is at least 12 carbon atoms in length being especially preferred.

Those of skill in the art recognize that the quantity of cationic surfactant employed in the practice of the present invention can vary widely. Typically, the quantity of cationic surfactant falls in the range of about 0.1 up to 3 wt % of the organic fraction of said cyanate ester-containing composition.

Exemplary quaternary ammonium compounds include distearyldimethylammonium salts, hexadecylpyridinium salts, hexadecyldimethylphenylammonium salts, decyltrimethylammonium salts, dodecyltrimethylammonium salts, tetradecyltrimethylammonium salts, hexadecyltrimethylammonium salts, octadecyltrimethylammonium salts, eicosyltrimethylammonium salts, behenyltrimethylammonium salts, oleyltrimethylammonium salts, dioleyldimethylammonium salts, trioleylmethylammonium salts, didecyldimethylammonium salts, didodecyldimethylammonium salts, ditetradecyldimethylammonium salts, dihexadecyldimethylammonium salts, dioctadecyldimethylammonium salts, dieicosyldimethylammonium salts, dibehenyldimethylammonium salts, tridecylmethylammonium salts, tridodecylmethylammonium salts, tritetradecylmethylammonium salts, trihexadecylmethylammonium salts, trioctadecylmethylammonium salts, trieicosylmethylammonium salts, tribehenylmethylammonium salts, oleylhydroxyethyl imidazoline, and the like, as well as mixtures of any two or more thereof.

Presently preferred cationic surfactants include quaternary ammonium compounds where the sum of the alkyl groups adds up to at least twenty carbons and at least one of the hydrocarbon residues contains twelve or more carbons--ideally, where the sum of the carbon residues bonded to the central nitrogen is at least thirty-four and at least one of the hydrocarbon residues contains sixteen or more carbons.

Exemplary quaternary phosphonium compounds include tributylhexadecylphosphonium salts, hexadecyltriphenylphosphonium salts, and the like, as well as mixtures of any two or more thereof.

Tertiary amines contemplated for use in the practice of the present invention include tertiary amines having in the range of about 18 up to about 100 total carbon atoms. Preferably, at least one side chain of said tertiary amine is at least 16 carbon atoms in length.

Tertiary phosphines contemplated for use in the practice of the present invention include tertiary phosphines having in the range of about 18 up to about 100 total carbon atoms. Preferably, at least one side chain of said tertiary phosphine is at least 16 carbon atoms in length.

Those of skill in the art recognize that the quantity of tertiary amine and/or tertiary phosphine employed in the practice of the present invention can vary widely, typically falling in the range of about 0.1 up to 5 wt % of the organic fraction of said cyanate ester-containing composition.

Exemplary tertiary amines contemplated for use in the practice of the present invention include hexadecyldimethylamine, dihexadecylmethylamine, octadecyldimethylamine, dioctadecylmethylamine, dimethylbehenylamine, dimethyleicosylamine, N,N,N'-trimethyl-N'-hexadecyl-1,2-diaminoethane, N,N,N'-trimethyl-N'-octadecyl-1,2-diaminoethane, N,N,N'-trimethyl-N'-eicosyl-1,2-diaminoethane, N,N,N'-trimethyl-N'-behenyl-1,2-diaminoethane, N,N,N',N'-tetramethyl-1,20-diamino-(10,11-dioctyl)-eicosane, and the like, as well as mixtures of any two or more thereof.

Exemplary tertiary phosphines contemplated for use in the practice of the present invention include hexadecyldimethylphosphine, dihexadecylmethylphosphine, octadecyldimethylphosphine, dioctadecylmethylphosphine, dimethylbehenylphosphine, dimethyleicosylphosphine, N,N,N'-trimethyl-N'-hexadecyl-1,2-diphosphinoethane, N,N,N'-trimethyl-N'-octadecyl-1,2-diphosphinoethane, N,N,N'-trimethyl-N'-eicosyl-1,2-diphosphinoethane, N,N,N'-trimethyl-N'-behenyl-1,2-diphosphinoethane, and the like, as well as mixtures of any two or more thereof.

Amphoteric surfactants contemplated for use in the practice of the present invention include higher alkyl betaines, higher alkyl sulfobetaines, N-alkylaminopropionic acids, N-alkyliminodipropionic acids, imidazoline carboxylates, tertiary amine oxides, tertiary phosphine oxides, and the like, as well as mixtures of any two or more thereof.

Those of skill in the art recognize that the quantity of amphoteric surfactant employed in the practice of the present invention can vary widely, typically falling in the range of about 0.1 up to 2 wt % of the organic fraction of said cyanate ester-containing composition.

The presently preferred amphoteric surfactants for use in the practice of the present invention include higher alkyl betaines and higher alkyl sulfobetaines. An exemplary higher alkyl betaine is palmitamidopropyl betaine.

Exemplary higher alkyl sulfobetaines include isostearylamidopropylethyldimonium ethosulfate, cocodimethylammonium-3-sulfopropyl betaine, lauryldimethylammonium-3-sulfopropyl betaine, myristyldimethylammonium-3-sulfopropyl betaine, palmityldimethylammonium-3-sulfopropyl betaine, stearyldimethylammonium-3-sulfopropyl betaine, tallowdimethylammonium-3-sulfopropyl betaine, distearylmethylammonium-3-sulfopropyl betaine, cocoamidopropyldimethylammonium-3-sulfopropyl betaine, tallowamidopropyldimethylammonium-3-sulfopropyl betaine, and the like, as well as mixtures of any two or more thereof.

The rate of bleed of a cyanate ester adhesive on a substrate is strongly affected by temperature. The bleed rate for freshly dispensed adhesive at room temperature is usually extremely slow (although not zero). The curing process, however, requires a thermal excursion in order to develop the thermoset properties of the paste. The adhesive also generates additional heat during the cure exotherm. The cure of cyanate esters is particularly exothermic (approximately 700 joules per gram--depending on the equivalent weight of the cyanate used). As a consequence of this heating, the initial stages of cure result in a marked drop in the viscosity of the cyanate ester monomer. The viscosity of the adhesive falls to a minimum just before the adhesive attains the gel point. Since the rate of bleed is accelerated when the fluid phase of the adhesive is at a low viscosity, one potential means to achieve resin bleed reduction is to speed the transition to the gel point. An increase in the rate of cure, therefore, would represent a reduction in the time window during which bleed is most likely to occur.

Polyfunctional compounds that can directly interact with (i.e., work in concert with) the cyanate ester monomer, or independently cure (to form a cross-linked network) in the presence of the cyanate ester monomer during the intial stages of cure would provide an opportunity to reduce bleed by accelerating the rate of crosslinking. For this purpose, compounds bearing a plurality of functional groups such as acrylates, methacrylates, hydroxyls, cyanates, maleimides, allyls, epoxies, and the like, as well as combinations thereof, can be employed.

For example, a polyfunctional cyanate would potentially offer the advantage of reduced gel times for the cyanate monomer system without introducing any new functionality to the thermoset cure. Three grades of polyfunctional cyanate ester oligomers (with anywhere from approximately three to nine cyanate functions per molecule) are available from Lonza Inc., Fair Lawn, N.J., under the designation of "Primaset PT Resins".

Another class of polyfunctional compounds that can be used to decrease the time required to attain the gel point includes polyvinyl compounds. The most preferred polyvinyl compounds are the esters of acrylic or methacrylic acid. It is desirable that these monomers contain at least two polymerizable functions per molecule. These monomers are generally soluble in or miscible with liquid cyanate ester blends. Examples of such monomers include bisphenol A dimethacrylate, bisphenol A bis (2-hydroxypropyl) methacrylate, 1,6-hexanediol dimethacylate, 1,10-decanediol dimethacylate, pentaerythritol triacrylate, trimethyolpropane trimethacrylate, tris (2-hydroxyethyl) isocyanurate trimethacrylate, pentaerythritol tetraacrylate, di-trimethylolpropane tetraacrylate, dipentaerythritol pentaacrylate, and the like. These molecules may be rapidly polymerized to generate a cross-linked network.

When polyvinyl compounds as described above are used, it is desirable to add a free radical catalyst to insure the proper cure of these monomers. It is furthermore desirable to select a catalyst that has a very low temperature onset for the generation of free radicals. Examples of such low-temperature free radical catalysts include benzoyl peroxide, diisononanoyl peroxide, lauroyl peroxide, di-(2-ethylhexyl) peroxydicarbonate, di-(4-tert-butylcyclohexyl) peroxydicarbonate, dimyristyl peroxydicarbonate, t-amyl peroxy-2-ethylhexanoate, and the like.

The acrylate and/or methacrylate monomers described herein do not co-cure with the cyanate ester constituents of the adhesive, but rather cure independently. The final thermoset, in this case, comprises an interpenetrating network of polyacrylate/methacrylate within the cyclotrimerized cyanate matrix. Surprisingly, the incorporation of as much as twenty weight percent of these monomers has been found to have little or no effect on the thermal decomposition onset temperature (measured via thermogravimetric analysis) for the cured adhesive.

The presently most preferred, non-cyanate, functional group is hydroxyl. Polyhydroxy functionalized compounds are capable of rapid reaction with cyanate functions to form (thermally reversible) imidocarbonate linkages according to Scheme I: ##STR1## Furthermore, imidocarbonates are believed to accelerate the rate of cyclotrimerization of cyanate monomers themselves. The presence of several reactive sites in the same molecule enhances cross linking and, therefore, the rate of viscosity increase during the early stages of cure.

It is highly desirable, when the polyfunctional compounds used have hydroxyl functional groups, they should also have little or no solubility in the cyanate ester monomer at room temperature. This property insures that the additive will have no deleterious effect on the potlife of the adhesive. One particularly useful additive having all of the desirable properties set forth herein is poly(4-hydroxystyrene) (PHS). A room temperature solubility test was run that consisted of suspending five percent by weight of finely powdered PHS in a room-temperature-stable, 85:15 liquid blend of 1,1-bis(4-cyanatophenyl)ethane (Arocy L-10 from Ciba) and 2,2-bis(4-cyanatophenyl)propane (Arocy B-10 from Ciba). The particle size distribution for the original powdered PHS was compared to the one obtained for the PHS that had been sitting in the liquid cyanate monomer blend for one week at room temperature. The average particle size for the original powder was 8.8 micrometers with a minimum and maximum particle size measured at 1.8 and 68.5 micrometers, respectively. The cyanate ester immersed particles had an average diameter of 6.5 micrometers along with maximum and minimum measurements at 1.8 and 66.1 micrometers, respectively. It was concluded from this that neither swelling nor significant dissolution of the PHS particles occurred during room temperature storage. It is also noteworthy that there was no detectable change in the viscostity of the cyanate monomer vehicle containing the powdered PHS after one week storage at room temperature.

It is believed that the PHS swells and/or dissolves significantly only upon heating. The cure acceleration property, therefore, was presumed to be dependent upon the PHS particle size present in the cyanate ester. Finer particles, therefore, should have a more pronounced accelerating affect on cure of the cyanate monomers. A test was conducted to determine the dependence of the gel time on the PHS particle size (see Example 1).

Additional polyfunctional compounds contemplated for use in the practice of the present invention include pentaerythritol, poly[glycidyl (meth)acrylate], polyvinyl alcohol, poly[2-hydroxyethyl (meth)acrylate], sucrose monostearate, sorbitan monooleate, 1,1,1-tris(hydroxymethyl)ethane, polyglycerol monooleate, polyglycerol dioleate, and the like, as well as mixtures of any two or more thereof.

Those of skill in the art recognize that the quantity of polyfunctional compound employed in the practice of the present invention can vary widely, typically falling in the range of about 0.5 up to 10 wt % of the organic fraction of said cyanate ester-containing composition.

The presently preferred polyfunctional compounds used to increase the rate of viscosity rise during cure include novolac resins, poly(4-hydroxystyrene), poly(2-hydroxyethyl methacrylate), poly(2-hydroxypropyl methacrylate), and the like. The preferred reactive lubricant includes 12-hydroxystearic acid.

An especially preferred polyfunctional compound contemplated for use in the practice of the present invention is poly(4-hydroxystyrene) (PHS). Typically, PHS contemplated for use in the practice of the present invention has a molecular weight in the range of about 1,000 up to 1,000,000.

In accordance with another embodiment of the present invention, there are provided compositions for attaching a device to a substrate. Invention compositions comprise:

monomer vehicle comprising at least one polycyanate ester monomer;

filler; and

a quantity of a bleed control agent sufficient to reduce resin bleed upon application of said composition to a substrate.

In accordance with still another embodiment of the present invention, there are provided methods for reducing resin bleed of cyanate ester-containing compositions upon application to a substrate. Invention methods comprise adding to cyanate ester-containing compositions a quantity of a bleed control agent sufficient to reduce resin bleed upon application of the resulting composition to a substrate.

Without wishing to be bound by any theory, it is believed that the major issues that impact resin bleed include the following:

1) Cleanliness of the substrate.

2) Surface roughness of the substrate.

3) Surface energy of the substrate.

4) Viscosity of the adhesive.

5) Surface tension of the adhesive vehicle.

6) Cure rate of the adhesive.

The first two factors identified above are beyond the control of the adhesive formulator. In accordance with the present invention, however, it has been found that various compositional modifications can have an impact on the remaining four issues. The following strategies, applied alone or in combination, provide a significant reduction and/or total elimination of resin bleed.

1) Addition of a small, but effective, amount of a cationic surfactant.

2) Addition of a small, but effective, amount of a compound capable of forming a cationic surfactant in situ.

3) Addition of a small, but effective, amount of an amphoteric surfactant.

4) Addition of a poly-functional compound that is capable of participating in a rapid, thermally initiated, reaction with the monomer vehicle.

5) The combination of stratagies (1), (2) or (3) listed above with strategy number (4).

6) The preparation of silver flake coated with a lubricant that has residual functionality capable of reacting with the monomer vehicle.

Presumably, resin bleed inhibition is a function of the formation of a continuous or semi-continuous film of the lubricant on the substrate surface. It is believed that this film significantly reduces the apparent surface energy of the substrate and thus reduces the driving force for the adhesive liquid phase to wet the surface.

It has been observed herein that the most effective bleed control agents are those that contain one or more higher alkyl substituents. The preferred hydrocarbon chain length is at least twelve carbons and the most preferred is at least sixteen carbons in length.

It appears that the higher alkyl chains also are harder to displace off of the substrate surface than their lower alkyl analogs. That is to say, the higher alkyl substituted quaternary ammonium compounds have an equilibrium concentration gradient strongly shifted toward the substrate surface.

Another advantage of cationic surfactants (e.g., quaternary ammonium compounds) over several of the compound types found in the prior art is the absence of reactivity with the monomers used in commercially important adhesive systems. For example, with the most preferred bleed inhibitors cited in U.S. Pat. No. 4,483,898 (i.e., perfluorooctanoic acid and 1H,1H-pentadecafluoro octylamine), the carboxylic acid function is capable of rapid reaction with many of the most common monomers used in die attach adhesives (including cyanate esters, cycloaliphatic epoxies, and glycidyl ether epoxies). The amine cited in '898 is even more reactive with epoxies and cyanates (e.g. the addition of a primary aliphatic amine to a cyanate ester at room temperature results in an instantaneous--almost explosive--reaction). This reactivity would have an obvious deleterious effect on the pot life of a cyanate ester adhesive system.

A significantly more serious limitation to the preferred exemplary compounds cited in '898 is the propensity of such compounds to generate fluoride ion contamination in the cured adhesive. The described amine compound has hydrogen residues vicinyl to (i.e. on a carbon immediately adjacent to) covalently bound fluorine. Such compounds are well known to be capable of eliminating hydrogen fluoride (HF). Elimination of HF would, in turn, generate significant quantities of silver fluoride in the presence of any silver oxide residues on a silver filler according to Scheme II:

    2 HF+Ag.sub.2 O→2 AgF+H.sub.2 O                     II

It is also very likely that under realistic use conditions (e.g. during cure and/or lid seal heating cycles) that the exemplary carboxylic acid from '898 would decarboxylate. The resulting monohydro-perfluorooctane would likewise be extremely prone toward elimination of hydrogen fluoride. The consequences of this would be disastrous for the reliability of the microelectronic device since the fluoride ion is considered to be extremely corrosive toward aluminum circuitry in the presence of even trace moisture conditions. Furthermore, it is not necessary that any of these fluoride ion generating reaction steps be very efficent since the quantity of this ion that can be tolerated is extremely low. The specification limit in the industry for water extractable fluoride ion is less than ten parts per million.

The invention will now be described in greater detail by reference to the following non-limiting examples.

EXAMPLE 1 Effect of Particle Size of Polyfunctional Compound on Resin Bleed

The base thermoset vehicle employed for the experiments summarized in Table 1 comprises a liquid cyanate ester mixture (i.e., an 85:15 mixture of L-10:B-10, i.e., 1,1-bis(4-cyanatophenyl)ethane and 2,2-bis(4-cyanatophenyl)propane, respectively) and 500 ppm (metals basis) of cobalt(III) acetylacetonate catalyst. Five percent by weight of various sieved fractions of poly(hydroxy styrene) (PHS) were added to this vehicle. The sieve fractions employed were -170 +270, -270 +325, -325 +500 and -500 mesh.

A gel point test was conducted by placing a 30.3±0.2 milligrams drop of each of the test compositions on 22×22 millimeter borosilicate microscope cover slips and then heating these samples on a hot plate fixed at various temperatures. The gel point, recorded according to this test, represented the first instant in time when a solid probe would no longer penetrate the surface of the sample drop. The results of that test are summarized in Table 1.

                  TABLE 1                                                          ______________________________________                                         Gel time (seconds) as a function of PHS particle size                                  PHS particle size, mesh                                                Temperature                                                                              -170    -270     -325         Control                                (°C.)                                                                             +270    +325     +500  -500   Vehicle                                ______________________________________                                         150       405     380      355   325    1220                                   160       140     189      127   125    340                                    170       68      80       70    65     255                                    180       29      29       31    21     90                                     200       14      17       13    16     24                                     215       13      13       11    11     21                                     ______________________________________                                    

It is apparent from these results that the gel point time is significantly shorter, at every test temperature, for all of the PHS-containing samples, relative to the control. What appeared to be a cure-rate-dependence on particle size was clear-cut for only the lowest temperature run. The compositions that contained the finer particle size distributions generally did have enhanced cure rates despite the presence of some striking anomalies. Differences in cure rates for the various samples were diminished at the highest cure temperatures.

EXAMPLE 2 Effect of Other Polyfunctional Compounds on Resin Bleed

Other polyfunctional compounds (besides PHS) were also investigated for their impact on cure time. Gel point measurements were made for all of these materials at a 5% by weight loading in the base vehicle described in Example 1. 0.5% of di-(4-tert-butylcyclohexyl) peroxydicarbonate free radical catalyst was also included in each of the compositions containing acrylate monomers. The cure temperature was fixed at 180°±2° C. Solid samples were sieved to -270 mesh and liquid samples were simply added to the base formulation neat. The results of this gel point testing are summarized in Table 2.

                  TABLE 2                                                          ______________________________________                                         Gel Point Times for Several Polyfunctional Additives                                                     Gel Point Time                                       Designation                                                                               Compound       (seconds)                                            ______________________________________                                         2A         Poly(gylcidyl  85                                                              methacrylate)                                                       2B         Poly(vinyl alcohol)                                                                           85                                                   2C         Poly(2-hydroxyethyl                                                                           44                                                              methacrylate)                                                       2D         Sucrose monostearate                                                                          50                                                   2E         Sorbitan monooleate                                                                           58                                                   2F         1,1,1-         80                                                              tris(hydroxymethyl)                                                            ethane                                                              2G         Polyglycerol   35                                                              monooleate                                                          2H         Polyglycerol   57                                                              dioleate                                                            2I         Poly(4-        35                                                              hydroxystyrene)                                                     2J         Primaset PT30  64                                                   2K         Pentaerythritol                                                                               18                                                              tetraacrylate                                                       2L         Pentaerythritol                                                                               14                                                              triacrylate                                                         2M         Control Vehicle                                                                               90                                                   ______________________________________                                    

At the loading levels employed, and with this particular base formulation, the cure rate increase for the poly(glycidyl methacrylate) and the poly(vinyl alcohol) additives appeared to be insignificant, relative to control. In contrast, use of the polyfunctional cyanate (Primaset PT 30; 2J) did have a significant impact on the cure rate. One attractive feature inherent to this gel rate enhancer is that no new functionality is introduced to the system. The six most impressive cure rate accelerants in this test were pentaerythritol triacrylate (2L), pentaerythritol tetraacrylate (2K), polyglycerol monooleate (2G), poly(4-hydroxystyrene) (2I), poly(2-hydroxyethyl methacrylate) (2C), and sucrose monostearate (2D). Of these, the polyglycerol monooleate would not be particularly preferred due to a propensity to undergo a gel-like phase separation within minutes of mixing, and also since the room temperature stability for formulations containing this additive was not particularly high (the same phenomenon (i.e., relatively low room temperature stability) was also observed with the polyglycerol dioleate-containing formulation). No apparent viscosity change occurred with any of the other samples in this test after several days storage at room temperature.

The gel point recorded for the acrylate containing systems was totally a function of the free radical cure of these added (non-cyanate) monomers. Both of these samples (i.e., 2K and 2L) formed a gel network with extreme rapidity. There was, however, some syneresis (i.e., a thin film of uncured cyanate exuded out to the surface of the initially formed gel).

EXAMPLE 3 Addition of More Reactive Cyclotrimerization Catalysts for Bleed Control

It is well known to those of skill in the art of cyanate ester chemistry that certain transition metal cure catalysts are more reactive than others in promoting cyclotrimerization of cyanate ester monomers. An increase in the reaction rate would reduce the time required for the development of a gel network once cure is commenced. Metal carboxylates and/or acetylacetonates (AcAcs) that are noted for high rates of cure include zinc(II), copper(II), silver(I), iron(III), manganese(II) and (III), and nickel(II). The most preferred among these is Cu(II), in part, because it does not promote hydrolysis of the cyanate ester (either in the pre-cured or cured state).

Accordingly, a test was conducted to determine what effect the substitution of copper(II) acetylacetonate (Cu(II)AcAc) for cobalt(III) acetylacetonate (Co(III)AcAc) would have on resin bleed. Paste compositions were prepared that contained 80% by weight silver flake in a cyanate ester monomer vehicle. The silver flake consisted of a blend of 68.2% SF84 (Degussa-Metz), 20.4% EA0095 and 11.4% EA0018 (both from Chemet corporation). The cyanate ester monomer mixture used consisted of 85% Arocy L-10 and 15% Arocy B-10 (both from Ciba-Geigy Corporation). Two separate cyanate ester vehicles were prepared by dissolving 500 parts per million (metals basis) of either Cu(II)AcAc or Co(II)AcAc into the combined cyanate monomers. The silver blend described above was then thoroughly mixed with each of the cyanate ester vehicles to create the two paste mixtures used in this experiment.

A gold plated coupon was fired at 350° C. to remove any organic residue (a process which had previously been shown to maximize bleed). Three equal sized (approximately 100 milligrams each) drops of the test paste (i.e., Cu catalyzed) were placed on the clean gold plated coupon as well as one drop of the control (Co catalyzed) paste. The part was then placed in a 150° C. oven for twenty minutes. Resin bleed was determined for each test spot. The bleed on the control paste was severe (approximately 187 mils). The maximum measured bleed for each of the test drops was 0 mils, 15 mils and 45 mils, respectively. Thus, the worst case bleed measured for the Cu(II)AcAc catalyzed composition was less than a quarter of that of the Co(III)AcAc catalyzed control. Even though the above example utilized copper(II) as the sole transition metal catalyst, any of the transition metal catalysts mentioned above, or mixtures of the same, would have a similar effect on bleed. Experience with the cyanate ester combination employed herein suggests that 500 ppm Cu catalyst (as the acetylacetonate) represents the preferred upper concentration limit for this metal. Higher than 500 ppm Cu(II)AcAc reduces the usable room temperature pot life of the final pastes to less than sixteen hours. It is also preferable to use the acetylacetonate rather than a copper metal carboxylate (especially toward the upper concentration limit) since the former has been reported to posses superior latent cure characteristics.

EXAMPLE 4 Screening of Additional Potential Bleed Control Agents

A screening test was conducted to determine what properties are most important for bleed control agents. Mixtures were made in which 0.5% by weight of each test compound was added to a liquid cyanate ester-containing control vehicle as described above in Example 1 (i.e., comprising an 85:15 mixture of L-10:B-10 and 500 ppm cobalt catalyst [on a metals basis--from Co(III)AcAc]).

A small droplet of each test mixture was carefully weighed onto a clean gold plated coupon (all coupons used had been fired through a 350° C. belt furnace profile under a nitrogen atmosphere, and all parts that had been subjected to this cleaning step were used within eight hours of firing). The weight of sample deposited for each mixture test was 0.7±0.1 milligram. All samples were cured on a hot plate, set at 190°±2° C., until the gel point had been attained. The diameter of the bleed region was measured on the cured samples and an approximate area of bleed was calculated based on this diameter. All bleed areas were then normalized with respect to the bleed measured for the control mixture (i.e. the bleed area deterimined for each sample was divided by the bleed area of the control mixture and this fraction was then multiplied by 100 to derive an area percent indexed against the control mixture). Table 3 summarizes the results from this test.

                  TABLE 3                                                          ______________________________________                                         Relative Bleed for Cyanate Ester Additives On Gold Coupons                                                     Relative                                       Designation                                                                             Additive               Area                                           ______________________________________                                         3A       None (control)         100                                            3B       Dimethyldioctadecylammonium                                                                           1.9                                                     bromide                                                               3C       Dimethyloctadecylamine oxide                                                                          68                                             3D       Perfluorooctanoic acid 8.4                                            3E       Tributylhexadecylphosphonium                                                                          4.7                                                     bromide                                                               3F       Dioctadecylmethylammonium-3-                                                                          30                                                      sulfopropylbetaine                                                    3G       Hexadecyltriphenylphosphonium                                                                         66                                                      bromide                                                               3H       Tridodecylmethylammonium Iodide                                                                       59                                             3I       Hexadecylpyridinium chloride                                                                          13                                                      monohydrate                                                           3J       Dodecylhexadecyldimethylammonium                                                                      66                                                      iodide                                                                3K       Tetrabutylammonium bromide                                                                            110                                            3L       Tetrabutylammonium borohydride                                                                        100                                            3M       Dodecyldimethyloctadecylammonium                                                                      2.1                                                     iodide                                                                3N       Dimethyldioctadecylammonium                                                                           41                                                      cyanate                                                               3O       Dimethyldioctadecylammonium                                                                           81                                                      nitrate                                                               3P       Trimethylamine oxide dihydrate                                                                        73                                             3Q       Perfluorooctanesulfonic acid                                                                          66                                                      tetrabutylammonium salt                                               3R       Dodecyldimethylammonium-3-                                                                            27                                                      sulfopropylbetaine                                                    3S       Dimethyloctadecylammonium-3-                                                                          2.4                                                     sulfoproylbetaine                                                     3T       1-(3-sulfopropyl)-2-   120                                                     vinylpyridinium betaine                                               3U       Dimethylmethacryloxyethylsulfo-                                                                       100                                                     propylammonium betaine                                                3V       N,N-dimethyloctadecylamine                                                                            3.3                                            3W       Dodecyltrimethylammonium chloride                                                                     7.6                                            3X       Dimethyldioctadecylammonium                                                                           21                                                      chloride                                                              3Y       N,N-dimethylhexadecylamine                                                                            6.8                                            3Z       Tridodecylamine        64                                             3AA      Trioctylphosphine oxide                                                                               100                                            3BB      Triisooctylamine       92                                             3CC      Dioctadecylmethylamine 46                                             3DD      N,N-dimethyl-N-stearylamido-                                                                          83                                                      propylammonium-3-sulfopropyl-                                                  betaine                                                               3EE      Tetronic 90R4 (BASF)   46                                             3FF      Tetronic 904 (BASF)    46                                             3GG      Tetronic 1107 (BASF)   59                                             3HH      Triphenylphoshine      83                                             3II      N,N-(2-hydroxyethyl)octadecyl                                                                         67                                                      amine                                                                 3JJ      N,N-(2-hydroxyethyl)behenylamine                                                                      109                                            3KK      N-behenylpiperidine    67                                             3LL      Tribenzylamine         29                                             3MM      Perfluorotributylamine 46                                             3NN      1H, 1H-perfluorooctylamine                                                                            30                                             3OO      N-Octadecylpyridinium iodide                                                                          41                                             3PP      N-behenylpyridinium bromide                                                                           3.5                                            3QQ      N,N'-dioctadecyl-N,N,N',N'-                                                                           21                                                      tetramethyl-1,2-ethanediamine                                                  diiodide                                                              3RR      N,N,N-triethyl-N-behenylammonium                                                                      30                                                      bromide                                                               3SS      N,N-dimethyl-N-hexadecyl-N-                                                                           30                                                      perfluorooctylammonium iodide                                         3TT      Perfluorooctanesulfonic acid                                                                          6.1                                            3UU      T-Carboxypropyl-polydimethyl-                                                                         30                                                      siloxane (PS402--United Chemical                                               Technologies, Bristol, PA)                                            3VV      N,N,N',N'-tetramethyl-1,20-                                                                           2.6                                                     diamino-(10,11-dioctyl)-eicosane                                      ______________________________________                                    

Most of the additives tested herein had a significant impact on resin bleed reduction in this experiment. Six of the test compounds, however, were found to have substantially no effect. Two of these, 3T (i.e., 1-(3-sulfopropyl)-2-vinylpyridinium betaine) and 3U (i.e., dimethylmethacryloxyethylsulfo-propylammonium betaine) appeared to be completely insoluble in the liquid cyanate ester vehicle. 3L (i.e., tetrabutylammonium borohydride) produced an immediate color change in the cyanate/catalyst mixture (presumably, this color change had something to do with a chemical interaction (i.e. probably reduction/oxidation) between the cobalt catalyst and the borohydride anion). While no specific observations were made that would account for why 3K (i.e., tetrabutyl ammonium bromide) and 3AA (i.e., trioctylphosphine oxide) were ineffective, it is believed that there is a minimum hydrocarbon segment length necessary to achieve effective bleed control, and the butyl and octyl substituents present in 3K and 3AA, respectively, are below this threshold.

The most effective bleed control additives included 3B, 3D, 3E, 3I, 3M, 3R, 3S, 3V, 3W, 3X, 3Y, 3PP, 3QQ, 3TT and 3VV (i.e., dimethyldioctadecylammonium bromide, perfluorooctanoic acid, tributylhexadecylphosphonium bromide, hexadecyl pyridinium chloride monohydrate, dodecyldimethyl octadecylammonium iodide, dodecyldimethylammonium-3-sulfopropylbetaine, dimethyloctadecylammonium-3-sulfopropylbetaine, N,N-dimethyloctadecylamine, dodecyltrimethylammonium chloride, dimethyldioctadecylammonium chloride, N,N-dimethylhexadecylamine, N-behenylpyridinium bromide, N,N'-dioctadecyl-N,N,N',N'-tetramethyl-1,2-ethanediamine diiodide, perfluorooctanesulfonic acid and N,N,N',N'-tetramethyl-1,20-diamino-(10,11-dioctyl)-eicosane, respectively). The bleed area observed for these samples were all well under thrity percent of that of the control. Two of these materials (3W and 3X) are quaternary ammonium chlorides. While chloride ion containing compounds would be unacceptable in products intended for use in electronic packaging, additives 3W and 3X are clearly seen to be effective for bleed control, and could readily be used in other (i.e., non-electronic) applications.

All of the highly effective bleed control compounds noted above, with the exception of 3D, 3V, 3Y, 3TT and 3VV are quaternary compounds with one or more hydrocarbon segment lengths of at least twelve carbon atoms. The tertiary amines (3V, 3Y and 3VV) also have a higher alkyl (C-16 or C-18 or higher) hydrocarbon residue. It is likely that tertiary amines are "quaternized" in situ by reaction with the low (but significant) levels of phenolic species known to exist in commercially available preparations of L-10. Tertiary amines are strong Lewis bases and would be readily protonated in the presence of a phenol. A reaction scheme for the in situ quaternization of tertiary amines by phenolic residues is shown in Scheme III: ##STR2## It is furthermore believed that unhindered (specifically, dimethylalkyl) tertiary amines (e.g., 3V, 3Y and 3VV) perform better since the in situ formation of quaternary ammonium compounds is much more facile in the absence of stearic interference. Additives 3D, 3Z, 3BB, 3MM and 3NN are cited in U.S. Pat. No. 4,483,898 (discussed above). Compound 3D is the only member of this group that performed well in the tests described herein. An equally promising result was obtained with perfluorooctanesulfonic acid (3TT), which is not within the scope of '898. This compound would have distinct advantage over 3D in that perfluoroalkylsulfonic acids are known in the art to be much more resistant to chemical and/or thermal degradation than their carboxylic acid counterparts.

There is an additional interesting observation that can be drawn from the results presented in Table 3. The bleed for formulations 3N and 3O, although significantly less than the control, were more than an order of magnitude greater than the measured values for 3B and 3M. Since the cation is identical for all four of these compounds, it is not clear why a difference of anion associated with the quaternary compound should have such a profound effect on bleed. However, it is suspected that it may have something to do with subtle solubility differences. It may be, for example, that both the cyanate and nitrate quaternary ammonium salts have greater affinity for the liquid cyanate monomer phase than either of their bromide or iodide counterparts. This difference in affinity could, in turn, shift the surface-to-liquid equilibrium concentration for the various additives. Presumably, this equilibrium is shifted away from the surface for the nitrate and cyanate salts, and toward the surface for the bromide and iodide salts.

EXAMPLE 5 Screening of Potential Bleed Control Agents in Filled Formulations

The results summarized in Table 3 suggest several classes of compounds that could be used to retard resin bleed in cyanate ester adhesives. Cyanate esters, however, are frequently used in the further presence of fillers. The most useful filler employed for preparation of electrically conductive adhesives is particulate silver. The use of silver, especially silver flake, introduces an additional potential complication into the adhesive system.

It is well known to those of skill in the art that commercially available silver flake is typically coated with one or more lubricants. These lubricants are used because they prevent the silver particles from welding together during the mechanical flaking process. Additionally, the presence of lubricants on the finished flake both promotes rapid dispersion of the silver flake in fluid vehicles and also prevents the agglomeration of flake particles during storage. The most pervasive lubricants used to process silver flake include fatty acids such as oleic and stearic acids. A portion of these lubricants are believed to become bound to the silver surface in the form of silver carboxylate salts. A large excess, however, of these lubricants typically remains on the surface of the silver flake as the free acids. These compounds, as well as their metal salts, are essentially anionic surfactants.

It is well known to those of skill in the art of surface chemistry that anionic and cationic surfactants are incompatable. Specifically, it is well documented that mixtures of these two types of surfactants will result in their mutual precipitation. Non-ionic compounds, such as fatty acid esters of glycerol, sucrose, sorbitol, and the like, would be greatly prefered as silver lubricants since there would not be any risk of incompatability with any of the quaternary bleed retarding agents.

In view of the above considerations, there was a concern that anionic surfactant/cationic surfactant incompatability would occur when silver filler was added to cyanate ester vehicles containing some of the more effective bleed control agents identified in Table 3. A particular silver filler of interest contains a mixture of 68.2% SF84 silver flake (from Degussa-Metz, Corporation), 20.4% EA0095 and 11.4% EA0018 silver flake (both from Chemet Corporation). The principle lubricant on the Degussa-Metz flake is non-ionic, while the lubricant on both of the Chemet flakes is a fatty acid. This silver flake mix was loaded at 80.0% by weight into the 3A, 3B, 3D, 3E, 3I, 3M, 3R, 3S, 3V and 3VV mixtures, as described in Table 3. These paste mixtures were then dotted onto freshly fired gold coupons. The parts were then cured in a 150°±5° C. oven for fifteen minutes. Resin bleed away from the fillet was measured for two test dots from each compostion, as well as the control paste (i.e., 3A) on every one of the test substrates. The results of these tests are presented in Table 4.

                  TABLE 4                                                          ______________________________________                                         Effect of Additives on Relative Bleed                                          from Silver Filled Cyanate Adhesive                                                                  % Bleed                                                                        Relative to                                              Designation           Control                                                  ______________________________________                                         3A--None (control)    100                                                      3B--Dimethyl dioctadecylammonium                                                                     94                                                       bromide                                                                        3D--Perfluorooctanoic acid                                                                           5.0                                                      3E--Tributyl hexadecylphosphonium                                                                    75                                                       bromide                                                                        3I--Hexadecylpyridinium chloride                                                                     66                                                       monohydrate                                                                    3M--Dodecyl           170                                                      dimethyloctadecylammonium-iodide                                               3R--Dodecyl dimethylammonium-3-                                                                      >200                                                     sulfopropylbetaine                                                             3S--Dimethyl octadecylammonium-3-                                                                    92                                                       sulfopropylbetaine                                                             3V--N,N-dimethyloctadecylamine                                                                       31                                                       3VV--N,N,N',N'-tetramethyl-1,20-                                                                     15                                                       diamino-(10,11-dioctyl)-eicosane                                               ______________________________________                                    

The results presented in Table 4 strongly suggest that significant incompatability exists between the quaternary bleed control agents contemplated for use in the practice of the present invention, and the lubricants employed with silver flake. All of the quaternary bleed control agents had significantly diminished performance in this test, compared to that reported in Table 3. Perfluorooctanoic acid (3D), which is itself an anionic lubricant, was unaffected. The second best performance seen in this test was for the tertiary amines, N,N-dimethyloctadecylamine (3V) and N,N,N',N'-tetramethyl-1,20-diamino-(10,11-dioctyl)-eicosane (3VV). It may be that these compounds retain more of their bleed control efficacy because they are able to neutralize at least a portion of the (excess) stearic acid lubricant, as per the general reaction scheme (Scheme IV): ##STR3##

The anti-bleed efficacy of most of the quaternary compounds was either significantly reduced (as in 3B, 3E, 3I, or 3S), relative to results with the unfilled samples (i.e., Example 4), or substantially obliterated (as in 3M and 3R). Presumably, the presence of the free fatty acid lubricants can indeed neutralize some or all of the anti-bleed efficacy of the quaternary onium compounds contemplated for use in the practice of the present invention. It is believed that the incompatibility of the cationic and anionic lubricants results in a decrease in the functional concentration of the quaternary compounds.

EXAMPLE 6 Screening of Combinations of Potential Bleed Control Agents in Filled Formulations

It appeared that an additional agent was needed to enhance the effectiveness of tertiary amines and/or quaternary onium compounds employed for resin bleed control. The bleed test for the silver pastes was repeated as outlined in Example 5. This time, however, six percent of the vehicle phase (selected from the various vehicle phases referred to in Table 3) was replaced by -325 mesh poly(4-hydroxystyrene). The results from this test are summarized in Table 5.

                  TABLE 5                                                          ______________________________________                                         Combined Effect of Additives and 6% PHS on Relative Bleed                                            % Bleed                                                                        Relative to                                              Designation           Control                                                  ______________________________________                                         3A--None (control)    100                                                      3B--Dimethyl dioctadecylammonium                                                                     8.3                                                      bromide                                                                        3D--Perfluorooctanoic acid                                                                           7.2                                                      3E--Tributyl hexadecylphosphonium                                                                    21                                                       bromide                                                                        3I--Hexadecylpyridinium chloride                                                                     14                                                       monohydrate                                                                    3M--Dodecyl           3.2                                                      dimethyloctadecylammonium iodide                                               3R--Dodecyl dimethylammonium-3-                                                                      170                                                      sulfopropylbetaine                                                             3S--Dimethyl octadecylammonium-3-                                                                    56                                                       sulfopropylbetaine                                                             3V--N,N-dimethyloctadecylamine                                                                       16                                                       3VV--N,N,N',N'-tetramethyl-1,20-                                                                     0.0                                                      diamino-(10,11-dioctyl)-eicosane                                               ______________________________________                                    

The addition of powdered poly(4-hydroxystyrene) improved the anti-bleed performance of all of the tertiary amine and/or quaternary compounds tested, indeed, the performance of some of the formulations improved remarkably. The single most impressive result was for the high molecular weight, di-tertiary amine, 3VV. The combination of powdered poly(4-hydroxystyrene) with 3VV resulted in the elimination of any detectable bleed on the parts tested. It is believed that the presence of the polyfunctional compound allows for the most efficient use of the tertiary amine and/or quaternary bleed control agents. Presumably, increasing the rate of cure reduces the opportunity for bleed. The combination of tertiary amine and/or quaternary compounds with polyfunctional curing agents is seen to be much more effective than the use of either additive alone.

EXAMPLE 7 Screening of Additional Combinations of Bleed Control Agents in Filled Formulations

It was next decided to investigate various polyfunctional cure rate accelerators in the presence and absence of quaternary onium compounds. These materials were tested using a silver filled formulation in order to best simulate a commercial cyanate adhesive system. The base vehicles for this formulation were identical to those summarized in Table 2 (i.e., using the same catalyzed 85:15 mixture of L-10:B-10 base with 5% by weight added polyfunctional compound). The bleed results for pastes made from these vehicles and 80% by weight of the silver flake mix described earlier (see Example 5) are presented in Table 6. None of the quaternary bleed control compounds were added to any of these formulations.

The test pastes were placed onto freshly fired gold plated coupons. Two equal sized drops of these paste compostions were placed on each of the coupons as well as a drop of the control (the cyanate ester vehicle and silver filler without any polyfunctional additives). All of the compostions were cured in an oven at 150°±5° C. for fifteen minutes. The solvent bleed from the adhesive fillet was determined at several different points. These values were averaged and then normalized with respect to the control paste.

                  TABLE 6                                                          ______________________________________                                         Evaluation of Polyfunctional Compounds on Relative Bleed                                            % Bleed Relative                                          Designation          Control                                                   ______________________________________                                         2A--Poly(glycidyl methacrylate)                                                                     79                                                        2B--Poly(vinyl alcohol)                                                                             180                                                       2C--Poly(2-hydroxyethyl                                                                             150                                                       methacrylate                                                                   2D--Sucrose monostearate                                                                            51                                                        2E--Sorbitan monoleate                                                                              38                                                        2F--1,1,1-tris(hydroxymethyl)ethane                                                                 94                                                        2G--Polyglycerol monooleate                                                                         15                                                        2H--Polyglycerol dioleate                                                                           21                                                        2I--Poly(4-hydroxystyrene)                                                                          88                                                        ______________________________________                                    

The bleed of these formulations was lower than the control with the exception of 2B and 2C (poly(vinyl alcohol) and poly(2-hydroxyethyl methacrylate), respectively). The greatest bleed reduction (2G and 2H) was for the mono and dioleoyl esters of polyglycerol.

EXAMPLE 8 Combined Effect of Polyfunctional Compounds and Quaternary Onium Compounds on Relative Resin Bleed

Another series of tests were run to further examine the possible synergistic interaction of polyfunctional compounds and quaternary onium compounds. Thus, pastes were formulated from the vehicles described above for Example 2. Silver pastes were made from these vehicles using an 80% loading of the same silver flake mix as described previously. For this experiment, 0.65% of dimethyldioctadecylammonium bromide was also added to each of the test samples. Two controls were used to rate the efficiency of bleed control. The standard control was (as before) the catalyzed cyanate base vehicle mixed into an 80 weight percent silver loaded paste. The additional control run consisted of this same control composition, with the further addition of 0.65% of the above-described quaternary ammonium bromide. All bleed tests were run on clean gold coupons. The bleed results for each test composition were independently normalized to that of both controls. The results from this test are presented in Table 7.

                  TABLE 7                                                          ______________________________________                                         Combined Effect of Polyfunctional Compounds                                    and Quat on Relative Bleed                                                                       % Bleed %    Bleed                                                             Relative to  Relative                                        Designation       Control + Quat                                                                              to Control                                      ______________________________________                                         2A--Poly(glycidyl 28           7.6                                             methacrylate)                                                                  2B--Poly(vinyl alcohol)                                                                          47           12                                              2C--Poly(2-hydroxyethyl                                                                          102          34                                              methacrylate)                                                                  2D--Sucrose monostearate                                                                         31           9.1                                             2E-Sorbitan monooleate                                                                           48           23                                              2F--1,1,1-        79           49                                              tris(hydroxymethyl)ethane                                                      2G--Polyglycerol monooleate                                                                      52           27                                              2H-Polyglycerol dioleate                                                                         38           17                                              2I-Poly(4-hydroxystyrene)                                                                        1.4          0.58                                            ______________________________________                                    

The results obtained here demonstrate the marked synergism that occurs when both a quaternary bleed control agent and a polyfunctional compound are used together. The best results, in all cases, were obtained when both additives were present. The single most outstanding result was obtained using a combination of dimethyldioctadecylammonium bromide and poly(4-hydroxystyrene).

One additional unanticipated benefit that has been observed with respect to the combined use of quaternary ammonium bleed control agents with the above-described silver flakes and polyfunctional bleed control agents is a significant improvement in the electrical performance of the resulting adhesive. Thus, the average (based on ten parts tested for each group) post cure electrical resistance (through the die) for an untreated control paste was 0.062 ohms at a 1.45 mil bondline. The post cure electrical resistances for the control and 2I pastes at a 2.78 and 2.67 mil bondline were 83.3 and 3.35 ohms, respectively. This dramatic decrease in electrical resistance is considered to be quite advantageous for die attach applications that require electrical conductivity, and is an added unexpected benefit observed for the compositions claimed herein.

While the invention has been described in detail with reference to certain preferred embodiments thereof, it will be understood that modifications and variations are within the spirit and scope of that which is described and claimed. 

That which is claimed is:
 1. A composition for attaching a device to a substrate, said composition comprising:a monomer vehicle comprising at least one polycyanate ester monomer; a quantity of a tertiary amine sufficient to reduce resin bleed upon application of said composition to a substrate; wherein said tertiary amine has in the range of about 18 up to about 100 total carbon atoms, and wherein one side chain of said tertiary amine is at least about 16 carbon atoms in length; and optionally a metal catalyst.
 2. A composition according to claim 1 wherein said monomer vehicle comprises at least two monomers, and wherein at least one monomer is a polycyanate ester monomer.
 3. A composition according to claim 1 further comprising a filler.
 4. A composition according to claim 3 wherein said filler is thermally and/or electrically conductive.
 5. A composition according to claim 1 wherein said tertiary amine is hexadecyldimethyl-amine, dihexadecylmethylamine, octadecyldimethylamine, dioctadecylmethylamine, dimethylbehenylamine, dimethyleicosylamine, N,N,N'-trimethyl-N'-hexadecyl-1,2-diaminoethane, N,N,N'-trimethyl-N'-octadecyl-1,2-diamino-ethane, N,N,N'-trimethyl-N'-eicosyl-1,2-diaminoethane, N,N,N'-trimethyl-N'-behenyl-1,2-diaminoethane, N,N,N',N'-tetramethyl-1,20-diamino-(10,11-dioctyl)-eicosane, or a mixture of any two or more thereof.
 6. A composition for attaching a device to a substrate, said composition comprising:monomer vehicle comprising at least one polycyanate ester monomer; filler; and a quantity of a tertiary amine sufficient to reduce resin bleed upon application of said composition to a substrate; wherein said tertiary amine has in the range of about 18 up to about 100 total carbon atoms, and wherein one side chain of said tertiary amine is at least about 16 carbon atoms in length.
 7. A composition according to claim 6 wherein said monomer vehicle is present in an amount falling in the range of about 8 to 80 weight percent, based on the total weight of the composition.
 8. A composition according to claim 6 wherein said tertiary amine is hexadecyldimethyl-amine, dihexadecylmethylamine, octadecyldimethylamine, dioctadecylmethylamine, dimethylbehenylamine, dimethyleicosylamine, N,N,N'-trimethyl-N'-hexadecyl-1,2-diaminoethane, N,N,N'-trimethyl-N'-octadecyl-1,2-diamino-ethane, N,N,N'-trimethyl-N'-eicosyl-1,2-diaminoethane, N,N,N'-trimethyl-N'-behenyl-1,2-diaminoethane, N,N,N',N'-tetramethyl-1,20-diamino-(10,11-dioctyl)-eicosane, or a mixture of any two or more thereof.
 9. A method for reducing resin bleed of cyanate ester-containing compositions upon application to a substrate, said method comprising adding to said composition a quantity of a tertiary amine sufficient to reduce resin bleed upon application of said composition to a substrate; wherein said tertiary amine has in the range of about 18 up to about 100 total carbon atoms, and wherein one side chain of said tertiary amine is at least about 16 carbon atoms in length.
 10. A method according to claim 15 wherein said tertiary amine is hexadecyldimethyl-amine, dihexadecylmethylamine, octadecyldimethylamine, dioctadecylmethylamine, dimethylbehenylamine, dimethyleicosylamine, N,N,N'-trimethyl-N'-hexadecyl-1,2-diaminoethane, N,N,N'-trimethyl-N'-octadecyl-1,2-diamino-ethane, N,N,N'-trimethyl-N'-eicosyl-1,2-diaminoethane, N,N,N'-trimethyl-N'-behenyl-1,2-diaminoethane, N,N,N',N'-tetramethyl-1,20-diamino-(10,11-dioctyl)-eicosane, or a mixture of any two or more thereof.
 11. A composition according to claim 1 further comprising a polyfunctional compound.
 12. A composition according to claim 11 wherein said polyfunctional compound is poly(4-hydroxystyrene).
 13. A composition according to claim 1 wherein said tertiary amine is octadecyldimethylamine, dimethylbehenylamine or dimethyleicosylamine.
 14. A composition according to claim 1 wherein the quantity of tertiary amine falls in the range of about 0.1 up to about 10 weight percent of the organic fraction of said cyanate ester-containing composition.
 15. A composition according to claim 1 wherein the quantity of tertiary amine falls in the range of about 0.1 up to about 5 weight percent of the organic fraction of said cyanate ester-containing composition.
 16. A composition according to claim 6 further comprising a polyfunctional compound.
 17. A composition according to claim 16 wherein said polyfunctional compound is poly(4-hydroxystyrene).
 18. A composition according to claim 6 wherein said tertiary amine is octadecyldimethylamine, dimethylbehenylamine or dimethyleicosylamine.
 19. A composition according to claim 6 wherein the quantity of tertiary amine falls in the range of about 0.1 up to about 10 weight percent of the organic fraction of said cyanate ester-containing composition.
 20. A composition according to claim 6 wherein the quantity of tertiary amine falls in the range of about 0.1 up to about 5 weight percent of the organic fraction of said cyanate ester-containing composition.
 21. A method according to claim 9 wherein said composition further comprises a polyfunctional compound.
 22. A method according to claim 21 wherein said polyfunctional compound is poly(4-hydroxystyrene).
 23. A method according to claim 9 wherein said tertiary amine is octadecyldimethylamine, dimethylbehenylamine or dimethyleicosylamine.
 24. A method according to claim 9 wherein the quantity of tertiary amine falls in the range of about 0.1 up to about 10 weight percent of the organic fraction of said cyanate ester-containing composition.
 25. A method according to claim 9 wherein the quantity of tertiary amine falls in the range of about 0.1 up to about 5 weight percent of the organic fraction of said cyanate ester-containing composition. 